D6AC is a low alloy vacuum melted steel containing several other elements and with a carbon content of 0.42 to 0.48%. The hardenability of this alloy is better than that of AISI 4340 and D6AC can be heat treated to strengths ranging from 180 to 260 ksi.
Typical applications are for aircraft landing gear, axles or shafts and similar uses that require very good combination of fatigue strength and toughness.
D6AC machines like any of the other low alloy steels. Machining is best done with the alloy in the normalized and tempered condition. Machining, or grinding, of parts that have been heat treated to 200 ksi, or greater, require a 3 hour stress relief anneal after such machining.
Formability in the annealed condition is good.
D6AC may be welded by TIG method for thin sections or by Gas Metal Arc Welding (GMAW) for heavy sections using a filler rod of the same alloy. Care should be used to maintain preheat and interpass weld temperature at 450 to 550 F. Restrained weldments should subsequently be post-heated at 600 F, air cooled to 300 F and then, at once, be stress relieved in a furnace at 1000 F followed by re-normalizing and re-tempering.
Heat treat for hardening of this alloy must be preceded by a normalizing treatment at 1700 F followed by air cooling. The alloy can then be hardened by reheating to 1700 F followed by an oil quench in oil that is at 150 to 250 F. It is important to temper normalized or heat treated parts immediately so as to avoid cracking - see "Tempering".
The alloy is forgeable but no details are available - consult the alloy supplier.
Hot working may be done - consult the alloy supplier for details.
This alloy cold works readily in the annealed condition.
Anneal at 1500 F followed by air cooling.
Not applicable to this alloy.
Temper immediately after hardening by heating at a temperature that will give the desired strength level as follows: For 260 ksi temper at 575 F, for 200 ksi temper at 1100 F and for 180 ksi temper at 1150 F all for a minimum of 2 hours and all followe
See "Heat Treatment" and "Tempering".
Specific Gravity: 7.8
Specific Heat: 0.116
Melting Point: 2600
Thermal Conductivity: 30
To Send a Request for Quote, please Click Here, call 973.276.5000, or fax (973) 276 - 5050
Looking Ahead to Metals 2015
For CEO's, Purchasing Agents, Engineers, Machine Shops, OEMs, Business Owners ...
ISM's Purchasing Managers Report posted 10:00 AM ET May 1, 2013 PMI is 50.7%. New orders registered 52.3%