0.15 – 0.20
0.70 – 0.90
0.20 – 0.35
0.40 – 0.70
0.40 – 0.60
0.15 – 0.25
General characteristics of Alloy Steel 8617
Alloy steel 8617 is a case-hardening steel containing nickel, chromium and molybdenum as alloying elements. The alloy shows good strength and toughness properties, and has a slightly higher core strength than grade 8615.
This alloy may be used in the production of medium-strength parts such as forged camshafts, fasteners and gears.
This alloy is forged at a start temperature of around 2250ºF (1230ºC) and could be forged down to approximately 1700ºF(925ºC.) The alloy is air cooled after forging.
Annealing:For optimum machinabilty, an as-forged structure is normally sufficient for this grade of alloy steel. If this proves not to be the case then an iso-anneal from around 1650ºF (900ºC) to 1225ºF (660ºC) will improve machinability.
Normalizing:1700ºF (925ºC) and air cool. This is another method of improving machinability in this grade; normalizing might also be used prior to case hardening.
Hardening:The alloy will be austenitized at around 1550ºF (840ºC) and oil or water quenched depending upon section size and intricacy.
Tempering:to desired hardness, using temperatures based on past experience, following water or oil quench.
Machinability:This grade of alloy is readily machined following suitable cooling from forging or subsequent heat treatment.
Weldability:This steel may be welded by normal fusion methods, but prior to carburizing or hardening and tempering.
To Send a Request for Quote, please Click Here, or call 1.973.276.5000 or 1.800.600.9290 or fax 1.973.276.5050.